Material description

Material ID: SRK02-S1

Material type: Glass fibre reinforced aluminium foil with cellulosic paper backing, inorganic filler, and polymer coating.

Polymer: Polymers (-%)

 

Table 1. Estimated mass concentration of compounds.
CompoundMass Concentration (%)
Polymers (-)-

A. Material composition identification

A.1 Attenuated total reflection – Fourier transform infrared spectroscopy (ATR-FTIR)

Table 2. FTIR compound identification.
Identified Compounds
Polymers (-)
...
Figure 1 . FTIR spectra: Absorbance percentage versus wavenumber from the sample.
...
Figure 2. FTIR spectra: Absorbance percentage versus wavenumber from the sample and the identified compounds.

B. Thermogravimetric analysis

Table 3. Mass fraction of residue after thermal decomposition.
ConditionFraction of mass residue at 800°C
Non-oxidative (nitrogen)0.39
Oxidative (air)0.33
Table 4. Temperature and amplitude of main peaks in non-oxidative conditions.
Peak IDTemperature peak (°C)Amplitude of peak (°C-1)
Peak 12947.22 x 10-3
Peak 23272.66 x 10-3
Table 5. Temperature and amplitude of main peaks in oxidative conditions.
Peak IDTemperature peak (°C)Amplitude of peak (°C-1)
Peak 12857.23 x 10-3
Peak 24682.11 x 10-3
Peak 36699.3 x 10-4
...
Figure 4. Normalised mass (solid line) and derivative of the normalised mass (dashed line) in 150 ml min-1 of nitrogen and a heating rate of 20°C min-1.
...
Figure 5. Normalised mass (solid line) and derivative of the normalised mass (dashed line) in 150 ml min-1 of air and a heating rate of 20°C min-1 .